LS-504ET-3 热固化型导电银浆,用于ITO玻璃上做导电线路,有良好的导电性能,密着性,不易刮落 ITEMS LS-504ET-3 REMARKS COLOR / STATE Silver colored paste Visual VISCOSITY 40 ~ 50Pa.s/20°C, Viscotester VT-04 No.2 CURING CONDITION 150°C x 30 min. 150°C x 5 min. Circulating heat oven IR Curing Adhesion No problem Tape peeling(Glass ITO) SHEET RESISTIVITY �40 mΩ/c� Thickness 10μm Humidity test � + 10 % 60°C, 90%RH, 500hr Heat cycle test � + 10 % -20°C(4hr)~+80°C(4hr) After Coating � + 10%UV type � + 5% IR type UV 1000Mj/c� IR 130°C x 10 min.
|